Enhanced lube oil yield by low or no hydrogen partial pressure catalytic dewaxing of paraffin wax

ABSTRACT

Catalytic dewaxing of paraffin containing feeds with a catalyst having a certain pore structure, the feeds preferably produced from syn gas using a non-shifting Fischer-Tropsch catalyst, is accomplished in the substantial absence of added hydrogen, and a cyclic isomerization-catalyst regeneration process is provided.

FIELD OF THE INVENTION

[0001] This invention relates to a process of catalytically dewaxing paraffin containing hydrocarbons. More particularly, this invention relates to the production of lube base oils and diesel range oils with a pre-determined or pre-selected pour point or cloud point by catalytic dewaxing at low or no hydrogen partial pressures.

BACKGROUND OF THE INVENTION

[0002] The production of lube base oils and diesel range oils by the hydroprocessing of paraffin containing feeds is well known, e.g., hydroisomerization or hydrocracking of the paraffin feed. The processes are generally catalytic and are usually carried out at relatively high hydrogen pressures, e.g., >500 psi hydrogen partial pressure. Catalytic dewaxing is a form of hydroprocessing and involves paraffin isomerization and some hydrocracking.

[0003] Hydrogen has always been used in catalytic dewaxing mainly for promoting extended catalytic life by, e.g., reductive coke removal, see U.S. Pat. No. 4,872, 968. Hydrogen partial pressures in catalytic dewaxing ranges from about 200 psig to about 1,000 psig or more, e.g., see U.S. Pat. No. 5,614,079, and hydrogen partial pressures are usually in the higher end of the range—for reasons of catalyst life.

[0004] U.S. Pat. No. 5,362,378 discloses hydrogen partial pressures ranging from 72 to 2,305 psig for use with the large pore catalyst zeolite beta. This patent does not mention catalyst life or TIR, i.e., temperature increase required, necessary for maintaining product specifications, such as pour point or cloud point.

[0005] We have now found that a particular combination of features allows for conducting catalytic dewaxing at low or no hydrogen partial pressure and conditions that are selective to hydroisomerization with little or no hydrocracking.

SUMMARY OF THE INVENTION

[0006] In an embodiment of this invention, a paraffin containing feed, preferably a feed containing at least 80 wt % paraffins, can be catalytically dewaxed in the presence of a molecular sieve catalyst with one dimensional pore structures having an average diameter of 0.50 nm to 0.65 nm, and the difference between the maximum diameter and the minimum diameter is preferably ≦0.05 nm. The molecular sieve is exemplified by, for example, ZSM-23, ZSM-35, ZSM-48, ZSM-22, SSZ-32, zeolite beta, mordenite and rare earth ion exchanged ferrierite in conjunction with a dehydrogenation component. Preferably the molecular sieve catalyst is ZSM-48 (ZSM-48 zeolites herein include EU-2, EU-11 and ZBM 30 which are structurally equivalent to ZSM-48) with a dehydrogenation component; and the process is carried out in the substantial absence of added hydrogen. When hydrogen is present, either as a consequence of the reaction or as added hydrogen, the hydrogen partial pressure is less than 100 psig, preferably less than 70 psig. By substantial absence of added hydrogen is meant the only added hydrogen will be that which is inherently present in the feeds (usually <0.1 wt. % H₂)

[0007] In another embodiment of this invention, the catalyst is stable, that is, it can meet a predetermined pour point for at least two weeks.

[0008] In yet another embodiment of this invention, a cyclic process is provided wherein catalytic dewaxing occurs in a first zone while in a second zone catalyst is regenerated or rejuvenated, after which the feed is switched to the second zone where catalyst has been regenerated and the catalyst in the first zone is regenerated. Thus, a continuous catalytic dewaxing process may be provided.

BRIEF DESCRIPTION OF THE DRAWINGS

[0009]FIG. 1 is a schematic of a cyclic isomerization-catalyst regeneration process.

[0010]FIG. 2 is a plot showing the effect of hydrogen pressure on lube yield for isomerization of a Fischer-Tropsch wax over Pt/ZSM-48. Pour point (° C.) is on the abscissa and wt % on feed 700° F.+ lube yield is on the ordinate. The lines A, B, C, and D denote hydrogen partial pressures of 1000 psig, 500 psig, 300 psig, and 0 psig (no hydrogen), respectively.

[0011]FIG. 3 is a plot showing the effect of hydrogen pressure on gas yield for isomerizing a Fischer-Tropsch wax over Pt/ZSM-48. 700° F.+ lube pour point (° C.) is on the abscissa and is plotted against wt % on feed C₁-C₄ gas yield on the ordinate. Lines A, B, C, and D denote hydrogen partial pressures of 1000 psig, 500 psig, 300 psig, and 0 psig (no hydrogen), respectively.

[0012]FIG. 4 is a plot showing the effect of hydrogen pressure on lube viscosity for isomerization of a Fischer-Tropsch wax over Pt/ZSM-48. Pour point (° C.) on the abscissa is plotted against kinematic viscosity @ 100° C. in centistokes (cSt) on the ordinate. Lines A, B, and C denote 0 psig, 500 psig, and 1000 psig, respectively.

[0013]FIG. 5 is a plot showing the effect of hydrogen pressure on lube viscosity index for isomerization of a Fischer-Tropsch wax over Pt/ZSM-48. Pour point (° C.) on the abscissa is plotted against 700° F.+ lube viscosity index (VI) on the ordinate. The dots represent 1000 psig hydrogen, the x's represent 500 psig hydrogen, the filled triangles represent 300 psig hydrogen, and the open diamond represents 0 psig hydrogen (no hydrogen).

[0014] For the particular set of features described herein, reducing hydrogen partial pressure results in increased catalyst activity and increased yield of desired product with little hydrocracking (as evidenced by the low C₁-C₄ gas yields in FIG. 3).

DETAILED DESCRIPTION OF THE INVENTION

[0015] In FIG. 1, line 10 indicates a source of paraffin feed. Most preferably the feed is derived from a Fischer-Tropsch hydrocarbon synthesis process, particularly one that is operated in a non-shifting mode with a cobalt or ruthenium based catalyst, preferably a cobalt containing catalyst.

[0016] The feed is forwarded to first catalytic dewaxing zone 16 via open valve 12 and line 13. Hydrogen, to the extent desired, is fed through line 25. At the same time a source of an oxygen containing gas, i.e., oxygen, air, oxygen enriched air or oxygen in suitable proportion with inerts such as nitrogen, from source 30, is fed to a second zone 18 via open valve 32 and line 34 where deactivated catalytic dewaxing catalyst is regenerated. Regeneration off gases are removed through open valve 24 and line 26.

[0017] The catalytically dewaxed product from zone 16 is removed via open valve 44 through lines 40 and 48 to distillation zone 50 where products are recovered, e.g., diesel in line 52 and lube base stock in line 54.

[0018] Upon deactivation of the catalyst in zone 16, valves 12 and 44 are closed, oxygen from source 30 is fed to zone 16 via open valve 38 and line 36. Regeneration off gases are removed through open valve 20 and line 22.

[0019] Similarly, when zone 16 is being regenerated, valve 12 is closed and paraffin feed is delivered to zone 18 for catalytic dewaxing via open valve 14 and line 15. Hydrogen to the extent desired is fed through line 27. Product is recovered in line 42 and fed via open valve 46 and line 48 to distillation zone 50.

[0020] The cyclic nature of the process is denoted by open valves 12, 44, 32, and 24 and closed valves 14, 46, 38 and 20, and then upon deactivation of catalytic zone 16 with open valves 14, 46, 38, and 20 and closed valves 12, 44, 32, 24, whereupon catalytic dewaxing takes place in zone 18 and the catalyst in zone 16 is regenerated.

[0021] Catalytic dewaxing of paraffin containing feeds, preferably feeds produced from syn gas using a non-shifting Fischer-Tropsch catalyst, is accomplished at relatively low hydrogen partial pressures without substantial effect on the life of a ZSM-48 catalyst. The dewaxing process is essentially an isomerization process in which some hydrogen will be produced indigenously.

[0022] The feed that can be employed in various embodiments of this invention is a paraffin containing feed, preferably a feed that contains greater than 80 wt % n-paraffins, more preferably greater than 90 wt % n-paraffins, still more preferably greater than 95 wt % n-paraffins and still more preferably 98 wt % n-paraffins. The feed generally boils in the range 430° F.+, preferably 450° F.+, more preferably 450-1200° F. (minor amounts, e.g., less than about 10% of 1200° F.+ material may be present).

[0023] The feed is preferably low in unsaturates, that is, low in both aromatics and olefins. Preferably, the unsaturates level is less than 10 wt %, preferably less than 5 wt %, more preferably less than 2 wt %. Also, the feed is relatively low in nitrogen and sulfur, e.g., less than 50 wppm of each. Where a Fischer-Tropsch derived feed is employed, there is no need to pre-sulfide the catalyst, and indeed, pre-sulfiding should be avoided.

[0024] Most preferably, the feed is the product of a Fischer-Tropsch reaction that produces essentially n-paraffins, and still more preferably the Fischer-Tropsch process is conducted with a non-shifting catalyst, e.g., cobalt or ruthenium, preferably a cobalt containing catalyst.

[0025] The catalyst employed in the catalytic dewaxing step comprises a molecular sieve with one dimensional pore structure and a metal dehydrogenation component. The molecular sieves include such as ZSM-23, ZSM-35, ZSM-22, SSZ-32, zeolite beta, mordenite and rare earth ion exchanged ferrierite preferably a ZSM-48 catalyst containing a metal dehydrogenation functionality preferably supplied by the presence of platinum or palladium or both platinum and palladium, preferably platinum. The catalyst may be sulfided or unsulfided and is preferably unsulfided when sulfur can negatively interfere with associated processes, such as a Fischer-Tropsch process.

[0026] The molecular sieve catalyst support is described in J. Schlenker, et al., Zeolites, 1985, vol. 5, November, 355-358, hereby incorporated by reference. ZSM-48, in particular, is characterized by the X-ray diffraction pattern shown in Table 1 below. The material is further characterized by the fact that it exhibits a single line within the range of 11.8±0.2 Angstrom units. The presence of a single line at the indicated spacing structurally distinguishes ZSM-48 from closely related materials such as ZSM-12 (described in U.S. Pat. No. 3,832,449) which has two lines, i.e., a doublet, at 11.8±0.2 Angstrom units, and high silica ZSM-12 (described in U.S. Pat. No. 4,104,294) which also has a doublet at the indicated spacing. TABLE 1 Characteristic lines of ZSM-48 (calcined, Na Exchanged Form) Relative Intensity d(A) (I/I_(o)) 11.8 ± 0.2  S 10.2 ± 0.2  W-M 7.2 ± 0.15 W 4.2 ± 0.08 VS 3.9 ± 0.08 VS 3.6 ± 0.06 W 3.1 ± 0.05 W 2.85 ± 0.05  W

[0027] The values were determined by standard technique, i.e., radiation was K-alpha doublet of copper, and diffractometer equipped with a scintillation counter. The peak heights, I, and the positions as a function of two times theta, where theta is the Bragg angle, were determined by a compactor. From these the relative intensities, 100 I/I^(O), where I is the intensity of the strongest line or peak, and d(obs.), the interplanar spacing in A corresponding to the recorded lines were calculated. Table 1 gives the intensities in terms of the symbols W=weak, S=strong, VS=very strong, M=medium, and W-M=weak to medium (depending on the cationic form). Ion exchange of the sodium ion with other cations reveals substantially the same pattern with some minor shifts in interplanar spacing and variation in relative intensity. Other minor variations can occur depending on the silicon to aluminum ratio of the particular sample, as well as any subsequent thermal treatment.

[0028] ZSM-48 and methods for its preparation are described in U.S. Pat. Nos. 4,375,573; 4,397,827; 4,448,675; 4,423,021; and 5,075,269. The method of preparation described in U.S. Pat. No. 5,075,269 is particularly preferred, and is incorporated herein by reference. This method is for preparing a catalyst particularly suitable for the catalytic dewaxing process.

[0029] The zeolite, ZSM-48, and other utilizable zeolites such as ZSM-23, ZSM-35, ZSM-22, SSZ-32, zeolite beta, mordenite and rare earth ion exchanged ferrierite are usually employed with a dehydrogenation component in an amount of about 0.01 to 5.0 wt %, the component being manganese, tungsten, vanadium, zinc, chromium, molybdenum, rhenium, Group VIII metals such as nickel, cobalt, or the noble metals platinum and palladium. The noble metals are preferred components. Such component can be exchanged into the composition, impregnated thereon, or physically intimately admixed therewith. Such component can be impregnated in or onto the zeolite such as, for example, in the case of platinum, by treating the zeolite with a platinum metal-containing ion. Thus, suitable platinum compounds include chloroplatinic acid, platinous chloride and various compounds containing the platinum tetra-ammonia complex. Platinum and palladium are preferred hydrogenation components.

[0030] The compounds of the useful platinum or other metals can be divided into compounds in which the metal is present in the cation of the compound and compounds in which it is present in the anion of the compound. Both types of compounds which contain the metal in the ionic state can be used. A solution in which platinum metals are in the form of a cation or cationic complex, e.g., Pt(NH₃)₄Cl₂, is particularly useful.

[0031] Prior to its use, the ZSM-48 catalyst should be dehydrated at least partially. This can be done by heating to a temperature in the range of from about 100° C. to about 600° C. in an inert atmosphere, such as air, nitrogen, etc., and at atmospheric or subatmospheric pressures for between 1 and 48 hours. Dehydration can also be performed at lower temperature merely by placing the catalyst in a vacuum, but a longer time is required to obtain sufficient amount of dehydration. ZSM-48 is formed in a wide variety of particle sizes. Generally speaking, the particles can be in the form of a powder, a granule, or a molded product, such as extrudate having a particle size sufficient to pass through a 2 mesh (Tyler) screen and be retained on a 400 mesh (Tyler) screen. In cases where the catalyst is molded, such as by extrusion, the crystalline silicate can be extruded before drying, or dried or partially dried and then extruded.

[0032] As in the case of many other zeolite catalysts, it may be desired to incorporate the ZSM-48 with a matrix material which is resistant to the temperatures and other conditions employed in the dewaxing process herein. Such matrix materials include active and inactive materials and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and/or metal oxides e.g., alumina. The latter may be either naturally occurring or in the form of gelatinous precipitates, sols or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the ZSM-48, i.e., combined therewith, which is active, may enhance the conversion and/or selectivity of the catalyst herein. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate of reaction. Frequently, crystalline silicate materials have been incorporated into naturally occurring clays, e.g., bentonite and kaolin. These materials, i.e., clays, oxides, etc., function, in part, as binders for the catalyst. It is desirable to provide a catalyst having good crush strength since in a petroleum refinery the catalyst is often subject to rough handling which tends to break the catalyst down into powder-like materials which cause problems in processing.

[0033] Naturally occurring clays which can be composited with ZSM-48 include the montmorillonite and kaolin families which include the sub-bentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays, or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification.

[0034] In addition to the foregoing materials, ZSM-48 can be composited with a porous matrix material such as silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania, as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia, silica-alumina-magnesia and silica-magnesia-zirconia. The matrix can be in the form of a cogel. Mixtures of these components can also be used. The relative proportions of finely divided crystalline silicate ZSM-48 and inorganic oxide gel matrix vary widely with the crystalline silicate content ranging from about 1 to about 90 percent by weight, and more usually in the range of about 2 to about 80 percent by weight, of the composite.

[0035] In general, reaction conditions for dewaxing may vary widely even when the hydrogen partial pressures are maintained at low levels, e.g., 0 psig hydrogen. Thus, start of run temperatures may vary between about 550°-650° F. (288°-343° C.). End of run conditions can be defined by the nature of the product being produced, for example, when color specifications can no longer be met (an indication of catalyst deactivation), or when the pre-determined pour point can no longer be obtained, or the selectivity to isomerization is reduced as evidenced by an increase in methane yield due to hydrocracking. In general, however, end of run temperatures should be less than about 800° F. (427° C.), preferably less than about 750°F. (399° C.), more preferably less than about 725° F. (385° C.).

[0036] Catalyst deactivation is believed to be a result of coke formation on the surface of the catalyst, the coke covering or blocking access to the catalytic metal, as well as blocking the pores of the zeolite.

[0037] The catalyst may be regenerated by known methods including hot hydrogen stripping, coke removal by oxygen treatment or a combination of hydrogen stripping and oxygen treatment. (FIG. 1 illustrates a process where oxygen treatment is used to regenerate the catalyst).

[0038] Briefly, hydrogen stripping can be carried out with hydrogen or a mixture of hydrogen and an inert gas such as nitrogen, at isomerization reaction temperatures for a period of time sufficient to allow the catalyst to regain at least about 80%, preferably at least about 90% of its original lined out activity. Oxygen treatment can be carried out at calcining conditions, e.g., using air at temperatures from about 500° C. to 650° C., again for a period of time sufficient to allow the catalyst to regain at least about 80%, preferably at least about 90% of initial lined out activity after subsequent reduction.

[0039] In general, where hydrogen is present, other gases may be present, too, and will not interfere with the reaction. Such other gases may be nitrogen, methane, or other light hydrocarbons (that may be produced during the reaction). Total pressure may range up to 2000 psi, preferably 100-2000 psi, more preferably 150-1000 psi, still more preferably 150-500 psi. Hydrogen can make up 50-100% of total gas, preferably 70-100%, more preferably 70-90%. At the low hydrogen partial pressures recited herein, small amounts of olefins and aromatics may form when the isomerization is carried out in the substantial absence of hydrogen; and hydrofinishing, at well known conditions, may be necessary to remove these components.

[0040] The liquid hourly spare velocity is generally between about 0.1 and about 10, and preferably is generally between about 0.5 and 4. The hydrogen to feed (where hydrogen is used) ratio is generally between about 100 and about 10,000, and preferably between about 800 and about 4,000 standard cubic feet (scf) of hydrogen per barrel of fuel.

[0041] Alpha Value is an approximate indication of the catalytic cracking activity of the catalyst compared to a standard catalyst and provides a relative rate constant (rate of normal hexane conversion per volume of catalyst per unit time). The value is based on the activity of a silica-alumina cracking catalyst taken as an Alpha of 1 (rate constant=0.016 sec⁻¹). The test for Alpha Value is described in U.S. Pat. No. 3,354,078 in the Journal of Catalysis. vol. 4, p. 527 (1965); vol. 6, p. 278 (1966); and vol. 61. 395 (1980), each incorporated herein by reference. The Alpha Value of the catalyst prior to metal loading is preferably in the range of about 10 to about 50.

[0042] In the following examples, a Fischer-Tropsch wax having the properties shown in Table 2 below was used as feedstock for all isomerization reactions. TABLE 2 Fischer-Tropsch Wax Pour point, ° C. 82 IBP-700° F. (371.1° C.) (<C₂₄), wt % 3 700° F. (371. 1 ° C.)-1100° F. (593.3° C.) (C₂₄-C₆₀), 89 1100° F.+(593.3° C.) (C₆₀+), wt % 8

[0043] In all examples the catalyst was alumina bound (35 wt %), ZSM-48 crystals containing 0.6 wt % platinum (Pt dispersion based on hydrogen absorption: H/Pt=1.03).

[0044] Wax isomerization was performed using a micro unit equipped with a three zone furnace and a downflow trickle bed tubular reactor (0.5 inch ID). The unit was heat traced to avoid freezing of the high melting point feed wax. The catalyst extrudates were crushed and sized to 60-80 mesh. The reactor was loaded with a mixture of 15 cc sized catalyst and 5 cc of 80-120 mesh sand, which was then dried and reduced at 400° F. (204.4° C.) for one hour at one atmosphere, 240 cc/min hydrogen flow. Isomerization was conducted at 1.0 hr⁻¹ LHSV and at pressures indicated. When hydrogen was used as a co-feed, the hydrogen/feed ration was 5000 scf/bbl feed. In cases where no hydrogen was used, reactor pressure was maintained at 1000 psig. Isomerization reactions were started with feed at an initial temperature of 665° F. (351.7° C.) and hydrogen (where used) as noted. Material balances were carried out overnight for 16-24 hours after 8-12 hour line out period. Reactor temperature was gradually changed to vary pour point.

[0045] Off gas samples were analyzed by GC using a 60 m DB-1 (0.25 mm ID) capillary column with FID detection. Total liquid products (TLP's) were weighed and analyzed by simulated distillation (M1567 or D2887). TLP's were distilled into IBP-330° F. (165.6° C.) naphtha, 330-700° F. (165.6-371.1° C.) distillate, and 700° F.+ (371.1° C.+) lube fractions. The lube fractions were analyzed further by simulated distillation (simdis) to ensure accuracy of the actual distillation operations. Pour point and cloud point of 700° F.+ (371.1° C.) lubes were measured using D97 and D2500 methods, respectively; viscosities were determined at both 40° C. and 100° C. according to D 445-3 and D-445-5 methods, respectively.

[0046] Hydrogen pressure was found to affect substantially both catalyst activity and product selectivity. Upon decreasing hydrogen pressure, catalyst activity increased, e.g., 25-30° F. (14-16.7° C.) where hydrogen pressure was reduced from 1000 psig to 300 psig. Similarly, selectivity to lube base stock (700° F.+, 371.1° C.) increased with decreasing hydrogen pressure. FIG. 2 shows that lube yield was higher at lower hydrogen pressure. A maximum lube yield (app. 90% at −12° C. pour point) was obtained in the absence of hydrogen. At the same time, the yields of lighter by-products, that is, light gas (C₁-C₄), naphtha, and distillate were decreased with decreasing hydrogen pressure. Thus, the increased lube yield is clearly a function of increased selectivity for the catalyst.

[0047] By virtue of the enhanced selectivity, there appears to be lower rates of cracking side reactions. As hydrogen pressure is reduced, catalyst activity increases and a lower reaction temperature is required to achieve a target, or pre-determined, lube pour point. Both factors, substantial absence of hydrogen and lower reaction temperature should reduce cracking, hydrogenolysis and thermal or catalytic cracking. Hydrogenolysis in the absence of hydrogen should be negligible. See FIG. 3 regarding gas yields.

[0048] Lube base stock viscosity at a given or pre-determined, pour point was higher, too, at lower hydrogen pressure, and reached a maximum with no hydrogen as co-feed; i.e., zero psig hydrogen partial pressure. For example, at −20° C. pour point, the 700° F.+ (371.1° C.+) lube base stock obtained without co-feeding hydrogen had a KV at 100° C. of 7.7 cSt which is significantly higher than the 6.7 cSt base stock obtained with a 1000 psig hydrogen pressure, as shown in FIG. 4.

[0049] Viscosity and viscosity index are two key properties of lube base stocks. FIG. 5 shows that lowering hydrogen partial pressure, even to 0 psig, essentially had no effect on viscosity index of the lube base stocks.

[0050] Table 3 below shows the results of isomerizing a Fischer-Tropsch wax, i.e., catalytic dewaxing in the absence of hydrogen. “MB” refers to material balance. TABLE 3 MB Number 1 2 3 4 Time on Stream, Days 62.5 64.5 65.6 66.6 Temperature, ° F. 630 625 620 620 Pressure, psig 1000 1000 1000 1000 LHSV, hr⁻¹ 1.0 1.0 1.0 1.0 WHSV, hr⁻¹ 2.3 2.2 2.2 2.2 H₂ @ inlet, scf/bbl 0 0 0 0 Product Yield, wt % Feed C₁-C₄ Gas, wt % 2.8 1.2 0.6 0.4 C₅-330° F. Naphtha, wt % 7.5 3.9 1.4 0.4 330-700° F. Diesel, wt % 18.0 12.0 8.0 6.0 700° F.+ Lube Yield, wt % 72.0 83.0 90.0 93.2 Total HC, wt % on Feed 100.3 100.1 100.1 100.0 Lube Properties Isolated Yield, wt % 70.8 82.3 86.0 88.4 KV @ 40° C., cSt 40.1 38.7 40.6 41.4 KV @ 100° C., cSt 7.39 7.44 7.85 8.10 Viscosity Index 152.1 162.1 168 173.5 Pour Point, ° C. D97 −42 −33 −12 3 TBP 5%, ° F. by D2887 770 779 798 838 TBP 50%, ° F. 913 924 923 947 TBP 95%, ° F. 1044 1050 1042 1070 MB Closure, wt % 100.0 100.0 100.0 100.2 

What is claimed is:
 1. A catalytic dewaxing process which comprises reacting a paraffin containing feed stock over a catalyst comprised of a molecular sieve with a one dimensional pore structure having an average diameter of 0.50 to 0.65 nm, and a metal dehydrogenation component at dewaxing reaction conditions and in the substantial absence of added hydrogen.
 2. The process of claim 1 wherein TIR is less than 25° F./year.
 3. The process of claim 1 wherein the hydrogen partial pressure is less than about 100 psig.
 4. The process of claim 3 wherein the hydrogen partial pressure is less than about 70 psig.
 5. The process of claim 4 wherein the paraffin containing feedstock contains greater than 80 wt % n-paraffins and boils in the range above 430° F. (221.1° C.).
 6. The process of claim 5 wherein the dehydrogenation component is platinum or palladium.
 7. The process of claim 6 wherein the process comprises a cyclic catalytic dewaxing-catalyst regeneration process wherein catalyst is provided in a first reaction zone and a second reaction zone, the paraffin containing feed is dewaxed in the first reaction zone for a pre-determined period after which the paraffin containing feed is transferred to the second zone for dewaxing at reaction conditions, and catalyst in the first zone is regenerated.
 8. The process of claim 7 wherein dewaxing occurs in the second zone for a pre-determined period after which the paraffin containing feed is transferred to the first reaction zone wherein dewaxing occurs over the regenerated catalyst, and the catalyst in the second zone is regenerated.
 9. The process of claim 8 wherein catalyst regeneration is effected by hydrogen stripping or oxygen treatment.
 10. The process of claim 5 wherein the product of the catalytic dewaxing process is a lube base stock or a diesel range material.
 11. The process of claim 10 wherein the product is subjected to hydrofinishing.
 12. The process of claim 11 wherein the molecular sieve is selected from the group consisting of ZSM-23, ZSM-35, ZSM-48, ZSM-22, SSZ-32, zeolite beta, mordenite, rare earth ion exchanged ferrierite and mixtures thereof.
 13. The process of claim 12 wherein the molecular sieve is ZSM-48. 